Product Description
Ceramic yarn guide
Textile ceramics are mainly produced from alumina ceramic materials, which have excellent comprehensive technical properties such as high mechanical strength, high hardness, low high-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.
Material option:
Steatite
Alumina up to 99.7 % or 95% alumina
Titania
Zirconia
Range of products:
Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Cut Eyelet, Step Eyelets, Tubes, Rods, Sleeve, Ring, Bush, Disc, Dish, Washer, Plates Trap Guide, Traverse Guide, Pig tail Guide, Dog tail Guide, Rollers, Oilers, Oiling Nozzles Cutters
Application :
Yarn manufacturing machines
Twister machines
Airjet looms
Circular looms
weaving machines
winder machines
Rope,Tap plants
Customized guides as per detailed drawings and specifications.
Production process of textile ceramics:
1: Making mould
2: Prepare material according to requirement.
3: Blending material
4: Extrude items
5: Fire about 48 hours (depending on the size of the product)
6: Sanding (polishing)
7: Pick out superior products for delivery
Material data:
| Item | Unit | 95% al2o3 | 99% al2o3 | Zirconia | Black Tio2 | Yellow Tio2 |
| Color | white,pink | cream,pink | white,black,yellow | Black | Yellow | |
| Density | g/cm3 | 3.65 | 3.9 | 6 | 4 | 4 |
| Flexural strength | MPA | 290 | 390 | 1300 | 70 | 70 |
| Compressive strength | MPA | 3300 | 3900 | 3000 | 600 | 600 |
| Vickers hardness | HV0.5 | 1800 | 2000 | 1150 | 900 | 900 |
| Thermal expansion cofficient | 10-6 K-3 | 5-8.3 | 5.4-8.3 | 10 | 8.5 | 8.5 |
| Thermal conductivity | w/mk | 23 | 28 | 2 | 25 | 25 |